The purpose of this study was to optimize the thickness of anodizing Aluminum coatings processed under pulse current mode through the Design of Experiments (DOE) method. Thickness measurement, polarization and electrochemical impedance spectroscopy were employed to take Thickness and corrosion behaviors of the anodized coatings into consideration. Also, Field-emission scanning electron microscopy (FE-SEM) was utilized to characterize the surface morphology of the coatings. It was found that the thickness of anodized coatings strongly depends on various parameters among which, time, temperature and pulse current parameters such as current density limit, frequency and duty cycle were considered in the present study. Analysis of variance (ANOVA) was used for estimating the coating thickness. Experimental results showed the maximum value for coating thickness was 62 µm being attained at the maximum and minimum current density of 6.28 and 1.55 A/dm2, a frequency of 150.5 Hz, time of 51 min, duty cycle of 81.5% and the bath temperature of 13.5 oC. Also, FE-SEM observation of the surface of anodized coatings showed that this optimum condition leads to a lower porosity amount. Polarization measurements showed that this lower porosity amount caused an increase in corrosion resistance of anodized coatings.
 Santos, L. Vojkuvka, J. Pallarés, J. Ferré-Borrull, L.F. Marsal, “In situ electrochemical dissolution of the oxide barrier layer of porous anodic alumina fabricated by hard anodization”, Electoral. Chem., vol. 632, no. 1-2, 2009, pp. 139-142.
 H.S. kim, D.H. Kim, W. Lee, S.H. Cho, J.H. Hahn, H.S. Ahn, “Tribological properties of nanoporous anodic aluminum oxide film”, Surf. Coat. Technol, vol. 205, no. 5, 2010, pp. 1431-1437.
 M. Salerno, N. Patra, R. Losso, R. Cingolani, “Increased growth rate of anodic porous alumina by use of ionic liquid as electrolyte additive”, Mater. Let. , vol. 63, 2009, pp. 1826-1829.
 W.X. Wei, D. L. Hong, “Preparation of PTFE composite anodic film on aluminium alloy 6061 using electrophoretic process”, Tribol. Mater. Surf. Interface., vol. 4, 2010, pp. 74−77.
 M. A. Song-Jiang, L. Peng, Z. Hai-Hui, F. Chao-Peng, K.Ya-Fei, “Preparation of anodic films on 2024 aluminum alloy in boric acid-containing mixed electrolyte”, Trans. Nonferrous Met. Soc. China, vol. 18, 2008, pp. 825-830.
 X. F. Zhu, D. D. Li, Y. Song, and Y. H. Xiao, “The study of oxygen bubbles of anodic alumina based on high purity aluminum”, Mater. Let, vol. 59, 2005, pp. 3160– 3163.
 H. Habazaki, H. Konno, K. Shimizu, S. Nagata, P. Skeldon and G. E. Thompson, “Incorporation of transition metal ions and oxygen generation during anodizing of aluminium alloys”, Corros. Sci, vol. 46, 2004, pp. 2041-2053.
 W. Lee, K. Schwirn, M. Steinhart, E. Pippel, R. Scholz and U. Gösele, “Structural engineering of nanoporous anodic aluminum oxide by pulse anodization of aluminium”, Nat. nanotechnol., vol. 3, 2008, pp. 234-239.
 M. Mirzaei and M.E. Bahrololoom, “Influence of pulse currents on the nanostructure and color absorption ability of colored anodized aluminum”, Vacuum, vol.99, 2014, pp. 277-283.
 X. Zhao, G. Wei, X. Meng, A. Zhang, “High performance alumina films prepared by direct current plus pulse anodisation”, Surf. Eng., vol. 30, 2014, pp. 455-459.
 C.K. Chung, W.T. Chang, M.W. Liao, H.C. Chang, “Effect of pulse voltage and aluminum purity on the characteristics of anodic aluminum oxide using hybrid pulse anodization at room”, Thin. Solid. Film. , vol. 519, 2011, pp. 4754-4758.
 I. Mohammadi, A. Afshar, “Modification of nanostructured anodized aluminum coatings by pulse current mode”, Surf. Coat. Technol., vol. 278, 2015, pp. 48-55.
 H. H. Shih and S. L. Tzou, Study of anodic oxidation of aluminum in mixed acid using a pulsed current”, Surf. Coat. Technol., vol. 124, 2000, pp. 278–285.
 W. Bensalah, M. Feki, M. Wery and H.F. Ayedi, “Thick and Dense Anodic Oxide Layers Formed on Aluminum in Sulphuric Acid Bath”, Mater. Sci. Technol., vol. 26, no. 2, 2010, pp.113-118.
 W. Bensalaha, K. Elleuch, M. Feki, M. Depetris-Wery and H.F. Ayedi, “Optimization of tartaric/sulphuric acid anodizing process using Doehlert design”, Surf. Coat. Technol., vol. 207, 2012, pp. 123–129.
 I. Imanieh, E. Yousefi, A. Dolati and M.R. Mohammadi, “Experiments Design for Hardness Optimization of the Ni-Cr Alloy Electrodeposited by Pulse Plating”, Acta Metall. Sin. (Engl. Let.), vol. 26, no. 5, 2013, pp. 558–564.
 R.G. Brereton, “Applied Chemometrics for Scientists”, John Wiley & Sons, Ltd, UK, 2007.
 E.R. Rene, M.S. Jo, S.H. Kim and H.S. Park, “Statistical analysis of main and interaction effects during the removal of BTEX mixtures in batch conditions, using wastewater treatment plant sludge microbes”, Environ. Sci. Tech, 4 (2007) 177-182.
 J. Antony, “Design of Experiment for Engineers and scientists”, Elsevier Science & Technology Books, New York, 2003.
 K. Yokohama, H. Konno, H. Takahashi and M. Nagayama, “Advantage of pulsed Anodizing”, Plat. Surf. Finish. Vol. 69, 1982, pp. 62-65.
 W. X. Wei and C. C. Yin, “Influence of oxidation heat on hard anodic film of aluminum alloy”, J. Trans. Nonfer. Met. Soc. China, vol. 22, no. 11, 2012, pp. 2707−2712.
 T. Aerts, J-B. Jorcin, I. D. Graeve and H. Terryn, “Comparison between the influence of applied electrode and electrolyte temperatures on porous anodizing of aluminium”, Electrochem. Acta., vol. 55, 2010, pp. 3957-3965.
 P. Chowdhury, A.N. Thomas, M. Sharma, H.C. Barshilia, “An approach for in situ measurement of anode temperature during the growth of self-ordered nanoporous anodic alumina thin films: Influence of Joule heating on pore microstructure”, Electrochim. Acta, vol. 115, 2014, pp. 657-664.
 M. García-Rubioa, P. Ocón, A. Climent-Font, R. W. Smith, M. Curioni, G. E. Thompson, P. Skeldon, A. Lavía and I. García, “Influence of molybdate species on the tartaric acid/sulphuric acid anodic films grown on AA2024 T3 aerospace alloy, Corros. Sci., vol. 51, no. 9, 2009, pp. 2034-2042.